• Document: REFRAKTORI ( BATU TAHAN API )
  • Size: 795.85 KB
  • Uploaded: 2019-03-14 08:27:45
  • Status: Successfully converted


Some snippets from your converted document:

REFRAKTORI ( BATU TAHAN API ) DEPARTEMEN DEPARTEMEN METALURGI METALURGI DAN DAN MATERIAL MATERIAL UNIVERSITAS UNIVERSITAS INDONESIA INDONESIA FAKULTAS FAKULTAS TEKNIK TEKNIK 2008 2008 DR.- DR.-ING. IR. DR.-ING. IR. BAMBANG BAMBANG SUHARNO SUHARNO REFRAKTORI (BATU TAHAN API) Tujuan Pengajaran „ Memahami material refraktori, teknologi pembuatannya dan aplikasinya dalam rekayasa Tugas : 15 Mid-Test : 35 Ujian Akhir : 45 Lain lain : 5 % DR.-ING. IR. BAMBANG SUHARNO 1 REFRAKTORI ( BATU TAHAN API ) „ Material inorganik natural maupun sintesis, tahan terhadap temperatur > 1500 oC tanpa perubahan bentuk atau melebur Syarat : Pada Temperatur tinggi dan berbagai kondisi: „ Mampu mempertahankan bentuk „ Mampu mempertahankan kekuatan Tujuan : „ Menahan laju perpindahan panas didalam dapur ( furnace ) ke luar DR.-ING. IR. BAMBANG SUHARNO REFRAKTORI ( BATU TAHAN API ) DR.-ING. IR. BAMBANG SUHARNO 2 REFRAKTORI ( BATU TAHAN API ) DR.-ING. IR. BAMBANG SUHARNO APLIKASI PADA INDUSTRI BAJA DR.-ING. IR. BAMBANG SUHARNO 3 APLIKASI PADA INDUSTRI TIMAH DR.-ING. IR. BAMBANG SUHARNO APLIKASI PADA INDUSTRI NICKEL DAN KERTAS NICKEL PAPER INDUSTRY INDUSTRY DR.-ING. IR. BAMBANG SUHARNO 4 APLIKASI PADA INDUSTRI CEMENT DR.-ING. IR. BAMBANG SUHARNO APLIKASI PADA INDUSTRI CERAMIC DR.-ING. IR. BAMBANG SUHARNO 5 APLIKASI PADA INDUSTRI ALUMINIUM DR.-ING. IR. BAMBANG SUHARNO APLIKASI PADA INDUSTRI PERMINYAKAN DR.-ING. IR. BAMBANG SUHARNO 6 APLIKASI PADA INDUSTRI PUPUK DR.-ING. IR. BAMBANG SUHARNO Sifat Sifat Refraktori yang Diperlukan „ Tahan terhadap suhu tinggi „ Tahan terhadap Perubahan suhu yang mendadak „ Tahan terhadap lelehan terak logam, kaca, gas panas „ Tahan terhadap beban pada kondisi perbaikan „ Tahan terhadap beban dan gaya abrasi „ Menghemat panas „ Memiliki koefisien ekspansi panas yang rendah „ Tidak boleh mencemari bahan yang bersinggungan DR.-ING. IR. BAMBANG SUHARNO 7 SIFAT – SIFAT REFRAKTORI Sifat-sifat yang diperlukan : „ High refractoriness „ Resistance to chemical reaction with any substance in contact during their service „ Ability to stand the load of the material under heat treatment in the furnace at the operating condition „ Resistance to abrasion due the flow of change , flame, flue dust , flue gases etc. The action of gases , such SO2, CO, Cl2, CH4,H2O, and volatile oxides and salt of metals . All are capable of penetrating and reacting with brick „ Resistance to thermal shock caused by heating and cooling „ Porosity ( its volume , size ) „ Low volume change at the service temperature ( both permanent or reversible) DR.-ING. IR. BAMBANG SUHARNO SIFAT – SIFAT REFRAKTORI Phisycal and thermal properties „ melting point „ Porosity „ Hot and cold strength „ Thermal expansion „ Heat conductivity „ Sintering temperature „ Shrinkage DR.-ING. IR. BAMBANG SUHARNO 8 REFRAKTORI Pemilihan Refraktori Untuk proses peleburan logam – Sulit, tetapi – Problem yang penting untuk diketahui Faktor-faktor dalam pemilihan : – Proses metalurgi (asam/basa) – Refraktoriness optimum choice – Heat loss – Economy DR.-ING. IR. BAMBANG SUHARNO REFRAKTORI Why ? Melting units are Unique ¾ Melting programe ¾ Metal qualities and quantities ¾ Melting practice – Continuous – No continuous – Acid or basic slag Important Factor for the life of refractory: ¾ The chemical composition of melt ¾ The type of furnace (EAF) ¾ The size of furnace DR.-ING. IR. BAMBANG SUHARNO

Recently converted files (publicly available):